Methyl methacrylate polymerization in a tubular reactor: product quality and reactor behavior
Fleury, P. A.; Meyer, T.; Renken, A.
1992

Résumé

A modified diffusional model of Me methacrylate polymn. at 130-170 Deg was described qual. Based on the polymn. and the reactor model, the stability behavior of a pilot recycle reactor was predicted. In pilot expts. under stable reactor conditions, polymer product with mean mol. wt. ? 250,000 was obtained. The polydispersity index was .apprx. 2 which indicated that concn. and temp. gradients in the reactor could be neglected. [on SciFinder (R)]

Détails

Titre Methyl methacrylate polymerization in a tubular reactor: product quality and reactor behavior
Auteur(s) Fleury, P. A. ; Meyer, T. ; Renken, A.
Publié dans 4th International Workshop on Polymer Reaction Engineering
Série DECHEMA Monographien, 127
Pages 31-8
Date 1992
Editeur Weinheim, VCH
Mots-clés (libres)
Note CAN 118:213649 35-4 Chemistry of Synthetic High Polymers Swiss Fed. Inst. Technol.,Lausanne,Switz. Journal 0070-315X written in English. 9011-14-7P (PMMA) Role: SPN (Synthetic preparation), PREP (Preparation) (prepn. of, in tubular reactor, product quality and reactor behavior in relation to)
Autres identifiant(s) Afficher la publication dans Web of Science
Laboratoires LGRC
GSCP
Le document apparaît dans Production scientifique et compétences > SB - Faculté des sciences de base > ISIC - Institut des sciences et ingénierie chimiques > GSCP - Groupe de sécurité chimique et physique
Production scientifique et compétences > SB - Faculté des sciences de base > SB Archives > LGRC - Laboratoire de génie de la réaction chimique
Travail produit à l'EPFL
Chapitres de livre
Publié
Date de création de la notice 2006-04-18