  4. Graphene nanoplatelets promoted CoO-based catalyst for low temperature CO2 methanation reaction
 
research article

Graphene nanoplatelets promoted CoO-based catalyst for low temperature CO2 methanation reaction

Zhong, Liping  
•
Pham, Thi Ha My  
•
Ko, Youngdon  
Show more
May 15, 2023
Frontiers In Chemical Engineering

Methanation of CO2 is an important reaction for reducing CO2 emissions in a power-to-gas system. Compared to cobalt supported on gamma-Al2O3, cobalt supported on graphene nanoplatelets (GNPs) showed significantly better performance for CO2 methanation. Cobalt supported on GNPs was capable of 15% conversion of CO2 to CH4 at temperatures below 250 degrees C, compared to 5% for cobalt supported on Al2O3. In situ thermogravimetric analysis (TGA) demonstrated that the Co/GNP catalyst was stable to 400 degrees C. The maximum catalyst massspecific CH4 yield was obtained at a Co loading of 5wt% on GNPs; however, high Co loading on GNPs deactivated the reactivity of the Co/GNP catalyst. Transmission electron microscopy (TEM) demonstrated that 5wt% Co/GNPs had the smallest and most dispersed cobalt nanoparticles. Excessive loading of cobalt tended to form isolated large Co nanoparticles. X-ray photoelectron spectroscopy (XPS) and Raman spectrometry revealed that more CoO phases were maintained on the surface of 5wt% Co/GNPs, indicating that the interaction between the Co and the GNPs had more of an impact on cobalt's redox capacity than did particle size, which ultimately affected cobalt's active phase during the CO2 reduction process. Furthermore, Raman spectrometry demonstrated that Co loading led to an increase in graphene defects. Higher Co loading on GNPs resulted in fewer interfaces between Co and GNPs due to the agglomeration of Co nanoparticles.

  • Files
  • Details
  • Metrics
Loading...
Thumbnail Image
Name

1160254.pdf

Type

Publisher's Version

Version

http://purl.org/coar/version/c_970fb48d4fbd8a85

Access type

openaccess

License Condition

CC BY

Size

2.49 MB

Format

Adobe PDF

Checksum (MD5)

3bd587f3d74c0026066ed784f972499b

Logo EPFL, École polytechnique fédérale de Lausanne
  • Contact
  • infoscience@epfl.ch

  • Follow us on Facebook
  • Follow us on Instagram
  • Follow us on LinkedIn
  • Follow us on X
  • Follow us on Youtube
AccessibilityLegal noticePrivacy policyCookie settingsEnd User AgreementGet helpFeedback

Infoscience is a service managed and provided by the Library and IT Services of EPFL. © EPFL, tous droits réservés