In-series sample methodology for permeability characterization demonstrated on carbon nanotube-grafted alumina textiles
In-plane permeability of small area (100 × 50 mm) alumina fiber woven fabrics grafted with aligned carbon nanotubes (CNT) was quantified by placing them in series with a glass mat of known permeability during a flow experiment. The methodology was first validated on a reference woven textile. Permeability values matched those obtained by a direct method within a margin of ±15%. Permeabilities of radial-aligned (short CNT, SCNT) and so-called ‘Mohawk’ (long CNT, LCNT) morphologies of the CNT-grafted samples were then measured and compared to the non-grafted alumina, showing a decrease attributed to a change in local textile structure as assessed in previous studies. Unsaturated permeability decreased by 77% after SCNT- and 88% after LCNT-grafting, while saturated permeability further decreased by 90% and 93%, respectively. The high ratio of unsaturated to saturated permeability (in the range of 1.14 – 2.89) implies that capillary wicking contributes largely to the impregnation of CNT-grafted fabrics.
1-s2.0-S1359835X21003493-main.pdf
Publisher's version
openaccess
CC BY-NC-ND
8.23 MB
Adobe PDF
3f12678a57a7c1263c6fc9839336f93a