The effect of sodium hydroxide on Al uptake by calcium silicate hydrates (C S H)

To reduce the CO2 emissions from cement production, Portland cement (PC) is partially replaced by supplementary cementitious materials (SCM). Reactions of SCM with PC during hydration leads to the formation of CSH with more silicon and aluminum than in PC, which affects the stability and durability of such concrete. Therefore, it is crucial to determine the role of aluminum on CSH properties to predict the formed hydrate phase assemblages and their effects on durability. Aluminum sorption isotherms including very low Al concentrations have been determined for CSH with Ca/Si ratios from 0.6 to 1.4. Elemental measurements were performed with ICP-MS and ICP-OES. The presence of secondary phases was investigated by using thermogravimetric analysis and XRD. Higher dissolved concentrations of Al were observed at increased alkali hydroxide concentrations and thus higher pH values. High alkali hydroxide led to an increased Al(OH)4- formation, which reduced the Al uptake in CSH. This comparable behavior of Al and Si towards changes in pH values, points toward the uptake of aluminum within the silica chain both at low and high Ca/Si ratios. A higher Al uptake in CSH was observed at higher Ca/Si ratios, which indicates a stabilizing effect of calcium in the interlayer on Al uptake.


Published in:
Journal of Colloid and Interface Science, 572, 246-256
Year:
Jul 15 2020
Note:
This is an open access article under the CC BY-NC-ND license.
Other identifiers:
Laboratories:


Note: The status of this file is: Anyone


 Record created 2020-05-12, last modified 2020-05-17

Final:
Download fulltext
PDF

Rate this document:

Rate this document:
1
2
3
 
(Not yet reviewed)