Abstract

Single crystal growth by chemical vapour transport has resulted samples with Fe1.35Ge stoichiometry. Structural study has shown that the large number of vacancies introduces an incommensuately modulated structure. The electrical resistivity is in the 200 mu Omega cm range at room temperature, and although the ferromagnetic transition temperature at 425 K is clearly visible, it hardly varies down to 4.2 K. It is suggested that the large number of vacancies (and the incommensurate modulation) introduce a strong backscattering, and the system is at the brink of a Mooij correlation. The thermal conductivity and Seebeck coefficient carry also the consequences of the high concentration of vacancies. (c) 2019 Elsevier B.V. All rights reserved.