Toward Annealing-Stable Molybdenum-Oxide-Based Hole-Selective Contacts For Silicon Photovoltaics

Molybdenum oxide (MoOX) combines a high work function with broadband optical transparency. Sandwiched between a hydrogenated intrinsic amorphous silicon passivation layer and a transparent conductive oxide, this material allows a highly efficient hole‐selective front contact stack for crystalline silicon solar cells. However, hole extraction from the Si wafer and transport through this stack degrades upon annealing at 190 °C, which is needed to cure the screen‐printed Ag metallization applied to typical Si solar cells. Here, we show that effusion of hydrogen from the adjacent layers is a likely cause for this degradation, highlighting the need for hydrogen‐lean passivation layers when using such metal‐oxide‐based carrier‐selective contacts. Pre‐MoOX‐deposition annealing of the passivating a‐Si:H layer is shown to be a straightforward approach to manufacturing MoOX‐based devices with high fill factors using screen‐printed metallization cured at 190 °C.

Published in:
Solar RRL, 2, 4, 1700227
Feb 19 2018
Other identifiers:

Note: The status of this file is: Anyone

 Record created 2018-05-15, last modified 2019-05-07

Download fulltextPDF
Download fulltextPDF
Rate this document:

Rate this document:
(Not yet reviewed)