Microstructure and flow stress evolution during hot deformation of 304L austenitic stainless steel in variable thermomechanical conditions

Most of industrial hot deformation processes are performed in variable conditions where the strain rate and/or deformation temperature are not constant. In this work, hot compression tests in both constant and varying strain rate conditions were performed on 304L austenitic stainless steel using a Gleeble 3800 machine. The variations in microstructure and flow stress during and after the transient deformation stage are carefully analysed. It is clearly shown that, following the abrupt increase of strain rate, both the flow stress and substructural changes are subjected to a transient period over strains of ~0.2, before reaching states similar to those developed through constant strain rate conditions at the new strain rate. When the strain rate was rapidly decreased, the flow stress transient stage extended over a lower strain interval than the substructure transient period. It is shown that local misorientation distributions are good indicators of the deformation microstructure of low SFE materials as they capture small variations in deformation structures which cannot be analysed from stress-strain curves alone.


Published in:
Materials Science and Engineering: A, 711, 600-610
Year:
2018
Publisher:
Elsevier
ISSN:
0921-5093
Keywords:
Laboratories:




 Record created 2017-12-12, last modified 2018-09-13


Rate this document:

Rate this document:
1
2
3
 
(Not yet reviewed)