ITO/MoOx/a-Si:H(i) Hole-Selective Contacts for Silicon Heterojunction Solar Cells: Degradation Mechanisms and Cell Integration
Molybdenum oxide is an efficient hole collector for silicon solar cells. However, its optoelectronic properties deteriorate during cell manufacturing. To assess this issue, the optoelectronic properties and microstructure of molybdenum oxide-based hole contacts are evaluated at different steps of the manufacturing process. Molybdenum oxide becomes more absorbing as it reduces when placed in contact with hydrogenated amorphous silicon, triggering the formation of a 2-nm thick SiOx layer, and when annealed after exposure to the plasma used to sputter the transparent conductive oxide. These changes in the contact properties result in a barrier that impedes hole transport when measuring I-V characteristics at room temperature. Nonetheless, cells still reach an efficiency of up to 20.7% when using a front metal electrode screen-printed at 210 degrees C (21.7% for reference cells). Above 60 degrees C, both molybdenum oxide-based and reference cells exhibit the same efficiency as this barrier to hole transport vanishes.
paper_886.pdf
Publisher's version
restricted
645.14 KB
Adobe PDF
88db41b7de79a73aa3e34cddfa7bb955
JPV_Analysis of aSi_MoOx_ITO front contacts for silicon heterojunction solar_final_QJ.pdf
Postprint
openaccess
Copyright
3.97 MB
Adobe PDF
09c22ec4bd4b7a7daa28660521c3ca5b