Influence of synthesis parameters on CCVD growth of vertically aligned carbon nanotubes over aluminum substrate

In the past two decades, important results have been achieved in the field of carbon nanotube (CNT) research, which revealed that carbon nanotubes have extremely good electrical and mechanical properties The range of applications widens more, if CNTs form a forest-like, vertically aligned structure (VACNT) Although, VACNT-conductive substrate structure could be very advantageous for various applications, to produce proper system without barrier films i.e. with good electrical contact is still a challenge. The aim of the current work is to develop a cheap and easy method for growing carbon nanotubes forests on conductive substrate with the CCVD (Catalytic Chemical Vapor Deposition) technique at 640 degrees C. The applied catalyst contained Fe and Co and was deposited via dip coating onto an aluminum substrate. In order to control the height of CNT forest several parameters were varied during the both catalyst layer fabrication (e.g. ink concentration, ink composition, dipping speed) and the CCVD synthesis (e.g. gas feeds, reaction time). As-prepared CNT forests were investigated with various methods such as scanning electron microscopy, Raman spectroscopy, and cyclic voltammetry. With such an easy process it was possible to tune both the height and the quality of carbon nanotube forests.

Fulltext

Related material