Domain and lattice contributions to dielectric and piezoelectric properties of Pb(Zr x , Ti 1− x )O 3 thin films as a function of composition
In situ reactively sputter deposited, 300-nm-thick Pb(Zrx,Ti1-x)O3 thin films were investigated as a function of composition, texture, and different electrodes (Pt,RuO2). X-ray diffraction analysis, ferroelectric, dielectric, and piezoelectric measurements were carried out. While for dielectric properties bulklike contributions from lattice as well as from domains are observed, domain wall contributions to piezoelectric properties are very much reduced in the morphotropic phase boundary (MPB) region. Permittivity and d33 do not peak at the same composition; the MPB region is broadened up and generally shifted to the tetragonal side.
1999 Hiboux propriétés électriques piézoélectriques PZT - composition - perso_1.pdf
Postprint
openaccess
3.02 MB
Adobe PDF
7dbe252e356d22c79e6de4e6ef493634
S0884291400052870.pdf
Publisher's version
openaccess
n/a
775.02 KB
Adobe PDF
29a5dfa15c86be7594c6097136ce84d9