Synthesis and Characterization of High-Photoactivity Electrodeposited Cu
We present a systematic study on the effects of electrodeposition parameters on the photoelectrochemical properties of Cu2O. The influence of deposition variables (temperature, pH, and deposition current density) on conductivity has been widely explored in the past for this semiconductor, but the optimization of the electrodeposition process for the photoelectrochemical response in aqueous solutions under AM 1.5 illumination has received far less attention. In this work, we analyze the photoactivity of Cu2O films deposited at different conditions and correlate the photoresponse to morphology, film orientation, and electrical properties. The photoelectrochemical response was measured by linear sweep voltammetry under chopped simulated AM 1.5 illumination. The highest photocurrent obtained was −2.4 mA cm−2 at 0.25 V vs RHE for a film thickness of 1.3 μm. This is the highest reported value reached so far for this material in an aqueous electrolyte under AM 1.5 illumination. The optical and electrical properties of the most photoactive electrode were investigated by UV−vis spectroscopy and electrochemical impedance, while the minority carrier lifetime and diffusion length were measured by optical-pump THz-probe spectroscopy.
Keywords: Li-Ion Batteries ; P-Type Cu2O ; Cuprous-Oxide ; Electrical Conductivity ; Electrochemical Deposition ; 2-Step Electrodeposition ; Terahertz Spectroscopy ; Controlled Morphology ; Cyclotron-Resonance ; Inorganic Materials
Record created on 2012-03-29, modified on 2016-08-09