Fast laser writing of copper and iridium lines from thin solid surface layers of metalorganic compounds
Laser direct writing of metal lines from solid metalorg. films coated on surfaces has been studied in three systems. Copper deposition from Cu(HCOO)2.2H2O was carried out at higher writing speeds than previously attained. Direct writing of iridium lines from two novel Ir-cluster films [Ir4(CO)11Br][N(C2H5)4] and [Ir6(CO)15][N(CH3)3C8H17]2 was demonstrated. The copper and iridium lines were written on Pyrex. It was found that inhomogeneities in the metalorg. layer are crucial to the quality of the deposited metal. Laser writing of iridium at several cm s-1 gives lines of about 10 mm width, with elec. resistivities of the order of 10 times the bulk value.
1989
43
54
60
Copyright 2003 ACS
CAPLUS
AN 1990:169909
CAN 112:169909
76-2
Electric Phenomena
Lab. Chim. Tech.,Ec. Polytech. Fed.,Lausanne,Switz. FIELD URL:
Journal
ASUSEE
written in English.
Electric conductors (copper and iridium lines, fast laser writing of, from organometallic thin solid surface layers)
REVIEWED