Wire-shaped magnetic mutilayers for 'current perpendicular to plane' magnetoresistance measurements
Electrodeposition of magnetic multilayers was achieved in the cylindrical pores of a nuclear track-etched polycarbonate membrane. An assembly of wires with an average diameter of 80 nm and a length of 6 μm was obtained. Multilayers in these wires were grown by pulsed deposition of (Co, Ni) and Cu. The high aspect ratio of the sample allowed us to measure the magnetoresistance with the current perpendicular to the planes. Magnetoresistance ratios higher than 20% at ambient temperature are reported. © 1995.
Type
research article
Authors
Blondel, A.
•
Meier, J.
•
Doudin, B.
•
•
Attenborough, K.
•
Evans, P.
•
Hart, R.
•
Nabiyouni, G.
•
Schwarzacher, W.
Publication date
1995
Publisher
Published in
Volume
148
Issue
1-2
Start page
317
End page
318
Peer reviewed
REVIEWED
EPFL units
Available on Infoscience
March 24, 2010
Use this identifier to reference this record