In situ reduction and oxidation of nickel from solid oxide fuel cells in a Titan ETEM

Solid Oxide Fuel Cells (SOFC) common technology is based on anode- supported cells composed of nickel-yttria stabilized zirconia (Ni-YSZ) cermet. The nickel is in oxide state (NiO) during SOFC production and is reduced to metallic nickel during the first operation. The microstructure influences the SOFC electrochemical performance as well as its stability for long-term use. Oxidation of the nickel catalyst can occur at high fuel utilization and due to air leakage. The volume change from Ni to NiO can be detrimental for the thin supported electrolyte. In situ transmission electron microscopy enables to acquire further knowledge on the mechanisms behind the reduction and oxidation of nickel in the Ni-YSZ SOFC anode. The in situ reduction and re- oxidation of the FIB prepared TEM lamellae is performed in a FEI Titan equipped with an environmental cell. The reduction started at 400°C under 1.4 mbar of hydrogen. The volume contraction due to NiO reduction is compensated by formation of nanoporosity in the Ni grain. Nanoporosity was previously observed by Waldbillig et al. during ex situ reduction of Ni-YSZ composite TEM lamellae.

Published in:
MC2009 Graz, Materials science, 3, 521-522
Presented at:
Microscopy Conference 2009, Graz, August 30-September 4, 2009

 Record created 2010-02-19, last modified 2018-01-28

Rate this document:

Rate this document:
(Not yet reviewed)