Background Si-doping effects on Zn diffusion-induced disordering in GaAs/AlGaAs multiple-quantum-well structures
Identical GaAs/Al0.2Ga0.8As multiple-quantum-well (MQW) structures uniformly doped with Si at various concentrations ranging from 1x10(17) to 1X10(19) cm(-3) are grown by molecular-beam epitaxy to study the effects of the background Si-doping level on the Zn diffusion-induced disordering process. After Zn diffusions at 575 degrees C for 4 and 16 h, the structures are investigated by secondary-ion-mass spectrometry, and by transmission electron microscopy on cleaved wedges of the sample. The results show that the totally and partially disordered regions are always behind the Zn diffusion front. A dependence of the effective Zn diffusivity and of the disordering rate of the structures on the background Si-doping level is observed. The effective Zn diffusivity and the disordering rate are significantly reduced with increasing background Si concentration. Before Zn diffusion, photoluminescence spectra of the Si-doped MQW structures exhibit an increase in intensity of the Si donor-column-III vacancy complex emission band with increasing Si-doping level. This indicates that the concentration of column-III vacancies in the MQW structures increases as the background Si concentration increases. After Zn diffusion, an important decrease in intensity of the column-III vacancy related emission band is observed on the photoluminescence spectra taken in the Zn-diffused regions. The systematical analysis of the photoluminescence spectra of the Zn-diffused MQW structures as a function of diffusion time and as a function of etching depth below the sample surface makes it possible to describe the physical processes occurring during Zn diffusion. A model based on the ''kick-out'' mechanism of Zn diffusion is proposed to explain the effect of the background Si-doping level on the effective Zn diffusivity. The model shows that the effective Zn diffusivity is controlled by the concentration of column-III interstitials behind the Zn diffusion front and by the donor concentration in the sample. During the incorporation of Zn into the crystal lattice, column-III interstitials are generated. The supersaturation of these interstitials behind the Zn diffusion front is responsible for the enhancement of Al-Ga interdiffusion. Since column-III interstitials and column-III vacancies can mutually annihilate, the concentration of column-III interstitial and column-III vacancy in the Zn-diffused region is reduced with increasing Si-doping level, leading to a retardation of Zn diffusion into the MQW structure. On the other hand, a decrease of the effective Zn diffusivity caused by an increase in donor concentration in the samples is also demonstrated. Our results give evidence for the Fermi-level effect and the interactions between different point defects during Zn diffusion-induced disordering of GaAs/AlGaAs multilayered structures. (C) 1996 American Institute of Physics.
WOS:A1996UG87600030
1996
79
8
4009
4016
Swiss fed inst technol, inst micro & optoelectr, ch-1015 lausanne, switzerland. cen grenoble, dopt, cea technol avancees, leti, f-38041 grenoble, france. Ky, NH, SWISS FED INST TECHNOL, LAB APPL OPT, CH-1015 LAUSANNE, SWITZERLAND.
ISI Document Delivery No.: UG876
Cited Reference Count: 28
Cited References:
BARAFF GA, 1985, PHYS REV LETT, V55, P1327
CAMRAS MD, 1983, J APPL PHYS, V54, P5637
CHEN B, 1994, PHYS REV B, V49, P2985
CINGOLANI R, 1989, PHYS REV B, V40, P2950
DEPPE DG, 1987, APPL PHYS LETT, V50, P998
DEPPE DG, 1988, J APPL PHYS, V64, R93
DINGLE R, 1978, APPL PHYS LETT, V33, P665
GOSELE U, 1981, J APPL PHYS, V52, P4617
HARRISON I, 1989, SEMICOND SCI TECH, V4, P841
KAJIKAWA Y, 1992, SEMICOND SCI TECH, V7, P1170
KY NH, 1991, J APPL PHYS, V69, P7585
KY NH, 1991, J APPL PHYS, V70, P3887
KY NH, 1992, PHYS REV B, V46, P6947
KY NH, 1993, J APPL PHYS, V73, P3769
KY NH, 1993, J APPL PHYS, V74, P5493
LAIDIG WD, 1981, APPL PHYS LETT, V38, P776
LEE JS, 1987, SEMICOND SCI TECH, V2, P675
LIVESCU G, 1988, IEEE J QUANTUM ELECT, V24, P1677
PAVESI L, 1992, J APPL PHYS, V71, P2225
PAVESI L, 1994, J APPL PHYS, V75, P4779
SCHUPPLER S, 1993, APPL PHYS LETT, V63, P2357
SKOLNICK MS, 1987, PHYS REV LETT, V58, P2130
SWAMINATHAN V, 1992, J APPL PHYS, V72, P4648
TAN TY, 1991, CRIT REV SOLID STATE, V17, P47
WANG C, 1992, PHYS REV LETT, V69, P3789
WIGHT DR, 1985, GALLIUM ARSENIDE MAT
WILLIAMS EW, 1972, SEMICONDUCTORS SEMIM, V8
YU S, 1991, J APPL PHYS, V69, P3547
Part 1
REVIEWED