Co-Zn-Mn chiral cubic magnets display versatile magnetic skyrmion phases, including equilibrium phases stable far above and far below room temperature, and the facile creation of robust far-from-equilibrium skyrmion states. In this system, compositional disorder and magnetic frustration are key ingredients that have profound effects on the chiral magnetism. Reported here are studies of the magnetism in Co6.75Zn6.75Mn6.5 by magnetometry, small-angle neutron scattering (SANS), magnetic diffuse neutron scattering and Lorentz transmission electron microscopy (LTEM). While features in magnetometry and LTEM often give standard indications for skyrmion formation, they are not readily observed from the measurements on this system. Instead, skyrmion lattice correlations are only revealed by SANS, and they are found to form an orientationally disordered structure in a minority fraction of the sample. The majority fraction of the sample always displays orientationally disordered helical spin correlations, which undergo further disordering along the radial direction on cooling below the critical temperature (T-c similar or equal to 102 K). The near-complete suppression of the skyrmion phase, and the process of disordering on cooling, are attributed to competing magnetic interactions that dominate over the ferromagnetic interaction expected to favour chiral magnetism in this system. These competing interactions start to develop above T-c and become further enhanced towards low temperatures. The present observations of co-existing and disordered magnetic correlations over multiple length scales are not unique to Co6.75Zn6.75Mn6.5 but are seemingly common to the family of Co-Zn-Mn compounds with finite Mn, and their accurate description presents a challenge for theoretical modelling. In addition, this study highlights a need for neutron instrumentation capable of the comprehensive measurement of magnetic correlations over expanded ranges of momentum transfer in such multiplelength-scale magnets.