Understanding variant selection and texture in additively manufactured red-gold alloys
Printing gold alloys parts is a challenge due to the high reflectivity and thermal conductivity of these materials. Recent studies show an improvement in printing gold using the Laser Powder Bed Fusion (L-PBF) process; however, the impact of the A1 -> L1(0) phase transformation on printed red-gold alloy has not been studied. In this work, 3D printed red-gold samples with different post-processing conditions have been heat-treated at 250 degrees C to investigate the effect of the sample stress states on variant selection, by Electron Backscatter Diffraction. Synchrotron X-ray diffraction experiments reveal the presence of a non-negligible amount of tetragonal phase in the as-build red-gold samples. The use of an intermediate heat treatment at 600 degrees C to eliminate small domains of tetragonal phase formed during the manufacturing process demonstrates that the crystallographic textures following heat treatment are highly dependent on the stress-state during the early stage of the phase transformation. (C) 2022 The Authors. Published by Elsevier Ltd on behalf of Acta Materialia Inc.
WOS:000788063900014
2022-04-01
211
114490
REVIEWED