Yu, JiweiWang, ZhangweiSaksena, AparnaWei, ShaolouWei, YeColnaghi, TimoteoMarek, AndreasRampp, MarkusSong, MinGault, BaptisteLi, Yue2025-01-242025-01-242025-01-242024-10-0110.1016/j.actamat.2024.1202802-s2.0-85200808785https://infoscience.epfl.ch/handle/20.500.14299/243497Quantitative analysis of microstructural features on the nanoscale, including precipitates, local chemical orderings (LCOs) or structural defects (e.g. stacking faults) plays a pivotal role in understanding the mechanical and physical responses of engineering materials. Atom probe tomography (APT), known for its exceptional combination of chemical sensitivity and sub-nanometer resolution, primarily identifies microstructures through compositional segregations. However, this fails when there is no significant segregation, as can be the case for LCOs and stacking faults. Here, we introduce a 3D deep learning approach, AtomNet, designed to process APT point cloud data at the single-atom level for nanoscale microstructure extraction, simultaneously considering compositional and structural information. AtomNet is showcased in segmenting L12-type nanoprecipitates from the matrix in an AlLiMg alloy, irrespective of crystallographic orientations, which outperforms previous methods. AtomNet also allows for 3D imaging of L10-type LCOs in an AuCu alloy, a challenging task for conventional analysis due to their small size and subtle compositional differences. Finally, we demonstrate the use of AtomNet for revealing 2D stacking faults in a Co-based superalloy, without any stacking-faults-relevant samples in the training dataset, expanding the capabilities for automated exploration of hidden microstructures in APT data. AtomNet can thus recognize challenging microstructures, including nanoprecipitates with diameters above 2 nm, LCOs with diameters of about 1–2 nm without obvious compositional segregation, and even unforeseen planar defects by analyzing atom-atom environments. AtomNet pushes the boundaries of APT analysis, and holds promise in establishing precise quantitative microstructure-property relationships across a diverse range of metallic materials.trueAlloy designArtificial intelligenceAtomic-scale characterizationCrystalline defectsLocal chemical orderingtext::journal::journal article::research article