Madagalam, MallikarjunBartoli, MattiaRosito, MicheleBlangetti, NicolaEtzi Coller Pascuzzi, MarcoPadovano, ElisaBonelli, BarbaraCarrara, SandroTagliaferro, Alberto2023-09-112023-09-112023-09-112023-08-2210.1002/sstr.202300163https://infoscience.epfl.ch/handle/20.500.14299/200532WOS:001051575300001In order to deepen the understanding of the role of transition metal oxides in electron transfer at the electrochemical interface, the performance of ZnxNi1-xFe2O4 (x = 0, 0.2, 0.4, 0.6, 0.8, 1) nanomaterials in electrochemical sensing is studied. Nanomaterials are synthesized by simple autocombustion synthesis procedure. Field-emission scanning electron microscopy characterization shows that the particles have a size between 30 and 70 nm with an average crystallite size between 24 and 35 nm. The bandgap energies of the nanomaterials, as estimated by UV-vis experiments, are in the 2.32-2.56 eV range. The valence band maximum is evaluated using X-ray photoelectron spectroscopy and the position of the conduction band minimum is estimated. The ZnFe2O4 sensor has the best performances: highest rate constant (13.1 & PLUSMN; 2.8 ms(-1)), lowest peak-to-peak separation (386 & PLUSMN; 2 mV), and highest sensitivity (37.75 & PLUSMN; 0.17 & mu;A mM(-1)). Its limit of detection (7.94 & PLUSMN; 0.04 & mu;M) is second best, and its sensitivity is more than twice the sensitivity of the bare sensor (16.7 & PLUSMN; 0.9 & mu;A mM(-1)). Nanomaterials energy bands mapping with the experimental redox potentials is performed to predict the electron transfer at the electrochemical interface, and the importance of surface states/defects is highlighted in the electron transfer mechanism.Chemistry, PhysicalNanoscience & NanotechnologyMaterials Science, MultidisciplinaryChemistryScience & Technology - Other TopicsMaterials Sciencebandgapferritesnanoparticlesrate constantssensitivityspinelferrite nife2o4 nanoparticlesband-gap energymagnetic-propertiesznfe2o4 nanoparticlescyclic voltammetryoxidative stressfacile synthesismfe2o4 mx-rayoxideUnraveling the Effect of the Chemical and Structural Composition of ZnxNi1-xFe2O4 on the Electron Transfer at the Electrochemical Interfacetext::journal::journal article::research article