Vacche, Sara DalleMolina-Gutierrez, SamanthaFerraro, GiuseppeLadmiral, VincentCaillol, SylvainLacroix-Desmazes, PatrickLeterrier, YvesBongiovanni, Roberta2024-06-192024-06-192024-06-192024-05-3010.1021/acssuschemeng.4c01365https://infoscience.epfl.ch/handle/20.500.14299/208707WOS:001236191500001A novel-biobased latex was synthesized by redox-initiated emulsion copolymerization of ethoxy dihydroeugenyl methacrylate with 5 wt % of a photosensitive methacrylate containing a coumarin group. A stable copolymer latex having 16 wt % solids content and a particle size of 53 nm was obtained. The copolymer had a T-g of 29 degrees C and was soluble in acetone. Coatings were obtained, and the effect of UVA irradiation was tested: the light-induced cross-linking of the copolymer by [2 + 2] cycloaddition of the coumarin pendant moieties was demonstrated by UV-visible spectroscopy. As a consequence of UVA-induced cross-linking, the copolymer became insoluble in acetone. The copolymer latex was combined with hemp-derived nanocellulose to obtain composite self-standing films by simple mixing in an aqueous medium followed by casting, evaporation of water, and hot pressing. The composite films were also successfully cross-linked by [2 + 2] cycloaddition, with an enhancement of barrier properties. The water vapor transmission rate of the cross-linked composite films with up to 45 wt % nanocellulose was 5 times lower than that of the hemp nanocellulose film, while further addition of nanocellulose increased permeability.Physical SciencesTechnologyBiobased CompositesBiobasedlatexBiomassfillerHemp NanocelluloseCoumarinCycloadditionWater Vapor Barriertext::journal::journal article::research article