TEM of antiferroelectric-ferroelectric phase boundary in (Pb1-xBax)(Zr1-xTix)O-3 solid solution
TEM and XRD have been used to characterise the antiferroelectric-ferroelectric phase boundary which exists in the (Pb1-xBax)(Zr1-xTix)O-3 solid solution close to the PbZrO3 end member. Electron diffraction patterns and XRD spectra from the antiferroelectric phase could be indexed according to the PbZrO3 structure with superlattice reflections typically present at the +/-1/4{hk0} pseudocubic positions. By XRD, the polar ferroelectric phase appealed to be rhombohedral but electron diffraction patterns showed the presence of superlattice reflections at the 1/2{hk0} positions, indicating that the unit cell size was doubled with respect to the simple perovskite lattice. The intensity of these reflections was observed to decrease with increasing Ba and Ti concentration. A combination of dark field and high resolution dark field images showed the presence of antiphase boundaries associated with these reflections which were highly mobile during il radiation in the electron beam. (C) 1997 The Institute of Materials.
WOS:000072378600001
1997
96
6
217
224
Reaney, Im Univ Sheffield, Dept Mat Engn, Mappin St, Sheffield S1 3JD, S Yorkshire, England Univ Sheffield, Dept Mat Engn, Sheffield S1 3JD, S Yorkshire, England Ecole Polytech Fed Lausanne, MX D Eclubens, Lab Ceram, CH-1015 Lausanne, Switzerland Oxley Dev Co Ltd, Ulverston LA12 9QG, Cumbria, England
Za578
Cited References Count:17
REVIEWED