000083820 245__ $$aTubular La0.7Ca0.3Fe0.85Co0.15O3-delta Perovskite Membranes, Part I: Preparation and Properties
000083820 269__ $$a2006
000083820 260__ $$c2006
000083820 336__ $$aJournal Articles
000083820 520__ $$aDense tubular self-supporting   La<sub>0.7</sub>Ca<sub>0.3</sub>Fe<sub>0.85</sub>   Co<sub>0.15</sub>O<sub>3-δ</sub>perovskite membranes were   prepared by thermoplastic extrusion. The rheological  behavior of the ceramic  mixture was studied. Non-deformed  tubes of 10 and 5mm diameter and 0.3- 0.8mm wall thickness  could be extruded. After sintering at 1100°C, the   membranes reached a relative density of over 98% with an  average grain size  of =.25μm. Flexural strenght, elastic  modulus, and fracture toughness of  sintered perovskite  ceramics were determined on test bars prepared by   injection molding from a thermoplastic mixture identical to  that used for  extrusion. The room-temperature flexural  strenght reached 215 MPa in  fourpoint bending, and the  fracture toughness was 1.6  MPa•m<SUP>0.5</SUP>
000083820 6531_ $$alenireactive
000083820 700__ $$aTrunec, Martin
000083820 700__ $$aCihlar, Jaroslav
000083820 700__ $$0241617$$aDiethelm, Stefan$$g101146
000083820 700__ $$0240166$$aVan herle, Jan$$g107971
000083820 773__ $$j89$$k3$$q949-954$$tJournal of the American Ceramic Society
000083820 8560_ $$falain.borel@epfl.ch
000083820 8564_ $$zURL
000083820 8564_ $$s540857$$uhttps://infoscience.epfl.ch/record/83820/files/LENI-ARTICLE-2006-005.pdf$$zn/a
000083820 909C0 $$0252044$$pLENI$$xU10315
000083820 909CO $$ooai:infoscience.tind.io:83820$$pSTI$$particle
000083820 937__ $$aLENI-ARTICLE-2006-005
000083820 973__ $$aEPFL$$rREVIEWED$$sPUBLISHED
000083820 980__ $$aARTICLE