3D laser shock peening as a way to improve geometrical accuracy in selective laser melting

One of the major drawbacks of selective laser melting (SLM) is the accumulation of tensile residual stresses (TRS) in the surface and subsurface zones of produced parts which can lead to cracking, delamination, geometrical distortions, and a decrease in fatigue life. 3D laser shock peening (3D LSP) is a novel hybrid method which introduces a repetitive LSP treatment during the manufacturing phase of the SLM process. In this paper, the ability of 3D LSP to convert TRS into beneficial compressive residual stresses and their subsequent effect on the geometrical accuracy of produced parts were investigated. Samples made of Ti6Al4V were manufactured with the 3D LSP process and treated with different processing parameters. Cuboidal samples were used for residual stress measurements, and the evolution of residual stresses was evaluated. Geometrical distortions were measured on bridge-like samples, and the influence on the final sample geometry was quantified. A significant improvement in geometrical accuracy resulting from reduced distortions was observed in all selected 3D LSP processing conditions.


Publié dans:
International Journal Of Advanced Manufacturing Technology, 101, 5-8, 1247-1254
Année
Apr 01 2019
Publisher:
London, SPRINGER LONDON LTD
ISSN:
0268-3768
1433-3015
Mots-clefs:
Laboratoires:




 Notice créée le 2019-06-18, modifiée le 2019-06-25


Évaluer ce document:

Rate this document:
1
2
3
 
(Pas encore évalué)