Oxygen transport in La0.5Sr0.5Fe1−yTiyO3−δ (y=0.0, 0.2) membranes

The influence of partial substitution of Fe with Ti on the oxygen transport properties of La1−xSrxFeO3 membranes was investigated in view of their application for oxygen separation. Samples of composition La0.5Sr0.5Fe1−yTiyO3−δ(y=0, 0.2) were prepared and their oxygen transport properties characterised by potential step relaxation and by oxygen permeation measurement in an air/argon gradient. With the first technique, chemical diffusion(D˜) and surface exchange (kS) coefficients were obtained by fitting of the current relaxation data to a single expression valid over the complete time range. The Ti-substituted composition gave slightly larger values of D˜ and kS. The trend was opposite for the measured oxygen permeation flux. In the latter experience, ordering of oxygen vacancies was observed at lower temperature, reducing significantly the performance of the material.


Published in:
Journal of Solid State Electrochemistry, 10, 8, 589-596
Year:
2006
Publisher:
Springer Verlag
ISSN:
1433-0768
Keywords:


Note: The status of this file is: Involved Laboratories Only


 Record created 2017-11-24, last modified 2018-01-28

External link:
Download fulltext
Publisher's version
Rate this document:

Rate this document:
1
2
3
 
(Not yet reviewed)