000199518 245__ $$aFree surface effects in TEM imaging of dislocation lines and loops in Fe
000199518 269__ $$a2014
000199518 260__ $$aLausanne$$bEPFL$$c2014
000199518 336__ $$aTheses
000199518 502__ $$aProf. H. Hofmann (président) ; Prof. C. Hébert (directrice) ; Prof. W. Curtin,  Prof. B. Devincre,  Dr R. Schäublin (rapporteurs)
000199518 6531_ $$atransmission electron microscopy
000199518 6531_ $$adiffraction contrast image
000199518 6531_ $$aimage stress effect
000199518 6531_ $$aanisotropy
000199518 6531_ $$adislocation loop
000199518 6531_ $$acolumn approximation
000199518 6531_ $$aCUFOUR
000199518 6531_ $$aSchaeublin-Stadelmann equations
000199518 700__ $$0(EPFLAUTH)215218$$aWu, Wenwang$$g215218
000199518 720_2 $$0240075$$aHébert, Cécile$$edir.$$g178548
000199518 8564_ $$s9103468$$uhttps://infoscience.epfl.ch/record/199518/files/EPFL_TH6262.pdf$$yn/a$$zn/a
000199518 909C0 $$0252032$$pLSME$$xU11814
000199518 909CO $$ooai:infoscience.tind.io:199518$$pDOI$$pSB$$pthesis$$pthesis-bn2018$$qDOI2
000199518 917Z8 $$x108898
000199518 917Z8 $$x108898
000199518 918__ $$aSB$$cICMP$$dEDMX
000199518 919__ $$aLSME
000199518 920__ $$a2014-6-24$$b2014
000199518 970__ $$a6262/THESES
000199518 973__ $$aEPFL$$sPUBLISHED
000199518 980__ $$aTHESIS