000184577 245__ $$aConductor Performance Qualification of TFKO3 Sample for ITER TF Magnet
000184577 269__ $$a2012
000184577 260__ $$bIEEE-Inst Electrical Electronics Engineers Inc$$c2012$$aPiscataway
000184577 300__ $$a4
000184577 336__ $$aConference Papers
000184577 520__ $$aTwo identical conductor samples were fabricated from 110 m length cable prepared for qualification of the manufacturing process for Phase II procurement of ITER TF conductor. Superconducting strand characteristics, cabling specifications, and the stainless steel jacket sections are described. Sample assembly and instrumentation of various voltage taps and temperature sensors have been prepared according to specified procedures for conductor performance qualification. The performance test program which was agreed to by the SULTAN working group was applied to the conductor samples. To assess the current sharing temperature (T-cs), standard analysis procedures were adopted. The T-cs of both samples at 68 kA with a background field of 10.78 T after a 1000 cyclic load are well above the acceptance criteria. Behavior of individual "star" voltage taps which are located at different positions and which are possible origins of rather large discrepancies in the T-cs of identical samples is discussed. The effective strain and the transition index of the samples are obtained from the experimental data.
000184577 6531_ $$aITER
000184577 6531_ $$aNb3Sn strand
000184577 6531_ $$aSULTAN
000184577 6531_ $$aTF conductor
000184577 700__ $$uNatl Fus Res Inst, Taejon 305333, South Korea$$aPark, Soo-Hyeon
000184577 700__ $$uNatl Fus Res Inst, Taejon 305333, South Korea$$aKwon, Soun Pil
000184577 700__ $$uNatl Fus Res Inst, Taejon 305333, South Korea$$aKim, Keeman
000184577 700__ $$aStepanov, Boris
000184577 700__ $$aBruzzone, Pierluigi
000184577 7112_ $$dSeptember 12-16, 2011$$cMarseille$$a22nd International Conference on Magnet Technology (MT))
000184577 773__ $$j22$$tIEEE Transactions On Applied Superconductivity$$k3
000184577 909C0 $$pCRPP
000184577 909C0 $$pSPC$$0252028$$xU10136$$xU12267$$xU12269$$xU12271$$xU10559$$xU12273$$xU10557$$xU12270$$xU10137$$xU10636$$xU12266$$xU10635$$xU10558$$xU12268$$xU12272
000184577 909CO $$pconf$$pSB$$ooai:infoscience.tind.io:184577
000184577 917Z8 $$x105317
000184577 917Z8 $$x112823
000184577 937__ $$aEPFL-CONF-184577
000184577 973__ $$rREVIEWED$$sPUBLISHED$$aEPFL
000184577 980__ $$aCONF