Examination of Japanese Mass-Produced Nb3Sn Conductors for ITER Toroidal Field Coils

The performances of six Nb3Sn conductors for the ITER Toroidal Field coils were tested. Four of them showed similar degradation rates of their current sharing temperatures T-cs over 1,000 electromagnetic cycles. By contrast, two of them showed sharp T-cs degradations at 50 cycles, after which their slopes became similar to those of the other four conductors. These two cables seemed to shrink under high magnetic fields during the first 50 cycles, which caused the sharp T-cs degradation. This shrinkage might arise from a decline in cable rigidity due to, for example, the deformation of strands or the breakage of the Nb3Sn filaments. The four mass-produced conductors had roughly the same AC loss before cycling. After 1,000 cycles, the AC losses of all the conductors decreased markedly to less than half of those before cycling, and the values became approximately the same. After the test campaign, the destructive inspection of two of the conductors made it clear that the conductor had shrunk by about 520 ppm under the high magnetic field during the test. It was also clarified that some strands were visibly deformed under the high magnetic field, whereas those under the low magnetic field did not look distorted. This plastic deformation of the strands could be one of the major reasons for the T-cs degradation with cyclic operation.


Publié dans:
IEEE Transactions On Applied Superconductivity, 22, 3
Présenté à:
22nd International Conference on Magnet Technology (MT), Marseille, September 12-16, 2011
Année
2012
Publisher:
Piscataway, IEEE-Inst Electrical Electronics Engineers Inc
Mots-clefs:
Laboratoires:
SPC
CRPP




 Notice créée le 2013-02-27, modifiée le 2019-08-12


Évaluer ce document:

Rate this document:
1
2
3
 
(Pas encore évalué)