Structure and properties of La-modified Na0.5Bi0.5TiO3 at ambient and elevated temperatures

The crystal structure and property changes of sodium bismuth titanate (Na0.5Bi0.5TiO3, NBT) piezoelectric ceramics are reported as a function of La modification (0.5-2.0 at. %) and increasing temperature using high resolution x-ray diffraction, permittivity, depolarization, and polarization and strain hysteresis measurements. La substitution is found to decrease the depolarization temperature of NBT (e.g., 1.5 at. % La substitution lowers the depolarization temperature by 60 degrees C relative to the unmodified composition) with little impact on the room temperature polarization and strain hysteresis. The room temperature structures of the various NBT compositions were modeled using a mixture of the monoclinic Cc space group and the cubic Pm (3) over barm phase, where the Pm (3) over barm phase is used to model local regions in the material which do not obey the long range Cc space group. With increasing La substitution, the lattice parameter distortions associated with the Cc phase approached that of the prototypical cubic unit cell and the fraction of the Pm (3) over barm phase increased. The relationship between these crystallographic changes and the depolarization behavior of La-modified NBT is discussed. (C) 2012 American Institute of Physics. []

Published in:
Journal of Applied Physics, 112, 5, 054111
Melville, American Institute of Physics

 Record created 2012-11-08, last modified 2020-07-30

Rate this document:

Rate this document:
(Not yet reviewed)