Neodymium-deficient nickelate oxide Nd1.95NiO4+ı as cathode material for anode-supported intermediate temperature solid oxide fuel cells

The neodymium-deficient nickelate Nd1.95NiO4+ı, mixed conducting K2NiF4-type oxide, was evaluated as cathode for solid oxide fuel cells. The electrochemical properties were investigated on planar Ni–YSZ anode-supported SOFC based on co-tape casted and co-fired HTceramix® cells. Using a layer of strontium doped lanthanum cobaltite as current collector, a current density of 1.31Acm−2 (at 0.70V) was obtained at 800 ◦C using hydrogen fuel with small single cells, after optimizing the cathode sintering temperature. Impedance spectroscopy measurements were performed; the different resistive contributions and the values of the corresponding equivalent capacities are discussed.


Publié dans:
Journal of Power Sources, 185, 2, 1218-1224
Année
2008
Mots-clefs:
Note:
doi:10.1016/j.jpowersour.2008.06.072
Laboratoires:


Note: Le statut de ce fichier est: Seulement EPFL


 Notice créée le 2009-01-08, modifiée le 2019-03-16

n/a:
Télécharger le document
PDF

Évaluer ce document:

Rate this document:
1
2
3
 
(Pas encore évalué)