Fracture toughness of TiAl alloys: A comparison of two gamma-a2 structures
Barbi, Nicolas; Diologent, Frederic; Goodall, Russell; Mortensen, Andreas; Kim, YW; Morris, D; Yang, R; Leyens, C
2008

Résumé

Toughness measurements of a Ti-45Al-2N4u-2Nb + 0.8%vol TiB2 alloy with a. near fully lamellar microstructure and a Ti-46Al-8Nb alloy with a convoluted microstructure are performed at 650 degrees C under vacuum according to ASTM Standard E1820. Respective values of K-Ic = 18 MPa root m and 20 MPa root m are found, with comparatively good repeatability the toughness of these two alloys is thus relatively similar, despite significant differences in miciostructure and crack path.

Détails

Titre Fracture toughness of TiAl alloys: A comparison of two gamma-a2 structures
Auteur(s) Barbi, Nicolas ; Diologent, Frederic ; Goodall, Russell ; Mortensen, Andreas ; Kim, YW ; Morris, D ; Yang, R ; Leyens, C
Publié dans STRUCTURAL ALUMINIDES FOR ELEVATED TEMPERATURES: GAMMA TITANIUM AND OTHER: METALLIC ALUMINIDES
Pages 89-96
Présenté à TMS 2008 Annual Meeting and Exhibition, New Orleans, March 9-13, 2008
Date 2008
Editeur WARRENDALE, PA 15086-7514 USA, MINERALS, METALS & MATERIALS SOC
Mots-clés (libres)
Autres identifiant(s) Afficher la publication dans Web of Science
Laboratoires LMM
Le document apparaît dans Production scientifique et compétences > STI - Faculté des sciences et techniques de l'ingénieur > IMX - Institut des matériaux > LMM - Laboratoire de métallurgie mécanique
Publications validées par des pairs
Papiers de conférence
Travail produit à l'EPFL
Publié
Date de création de la notice 2008-10-30

Actions