000124524 245__ $$aMolecular dynamics modeling of cavity strengthening in irradiated iron
000124524 269__ $$a2006
000124524 260__ $$c2006$$aFreiburg-Germany
000124524 336__ $$aConference Papers
000124524 520__ $$aOne of the most important problems in the field of nuclear industry is the relationship between irradiation-induced damage and the resulting induced mechanical response of the target metal and in particular ferritic base steels. In this work the molecular dynamics is used to simulate the nanoscale interaction between a moving dislocation and a defect, such as a cavity, as void or He bubble. The stress-strain curves are obtained under imposed strain rate condition using the atomic potentials based on the Fe potential of Ackland et al. 1997 for a void and He bubble as a function of He content and temperature. It appears that a 2 nm void is a stronger obstacle than a He bubble at low He contents, whereas at high He contents, the He bubble becomes a stronger obstacle. With increasing temperature the escape stress decreases and at the same time there is increasing degeneracy in the type of interaction.
000124524 700__ $$aGumbsch, Peter
000124524 700__ $$0245053$$g168673$$aHafez Haghighat, S.M.
000124524 700__ $$aSchaeublin, R.$$g109859$$0240066
000124524 7112_ $$dSeptember 18-22, 2006$$cFreiburg-Germany$$aMMM Multiscale Materials Modeling, 3rd Int. Conference
000124524 773__ $$tProceeding of the Third International Conference on Multiscale Materials Modeling$$q729-732
000124524 8564_ $$zURL$$uhttp://www.mmm2006.org/cms/front_content.php
000124524 909C0 $$xU12272$$xU12268$$pSPC$$0252028$$xU10558$$xU10635$$xU12266$$xU10636$$xU10137$$xU12270$$xU10557$$xU12273$$xU10559$$xU12271$$xU12269$$xU12267$$xU10136
000124524 909CO $$qGLOBAL_SET$$pconf$$pSB$$ooai:infoscience.tind.io:124524
000124524 917Z8 $$x148230
000124524 937__ $$aCRPP-CONF-2006-112
000124524 970__ $$a4094-CONF/CRPP
000124524 973__ $$rNON-REVIEWED$$sPUBLISHED$$aEPFL
000124524 980__ $$aCONF