A thin InAs layer grown in a quasi-two-dimensional film over InP reorganizes into islands if left to anneal under arsine. This surface transformation is inhibited at lower arsine fluxes. With increasing temperature, the surface transformation is activated as long as the effective arsine coverage is sufficient.