Growth and properties of transparent Pb(Zn-1/3, Nb-2/3)O-3-PbTiO3 single crystals with a cubic habitus
Transparent single crystals of Pb(Zn-1/3, Nb-2/3)O-3-PbTiO3 (PZN-PT) perovskite have been grown by the slow cooling method in a temperature gradient furnace. The optimization of growth techniques to crystallize PZN-PT with a cubic habitus is described in details. The growth temperature range and cooling rates was carried out in different lead fluxes, Crystal recovery from the residual flux was obtained by different techniques based on liquid flux elimination at the end of the growth process. The best transparent single crystals of PZN-PT, obtained by a cooling at 0.8 degrees C/h from 1150 degrees C to 930 degrees C, had a cubic habitus and a size of approx.: 4 x 4 x 2.5 mm(3). The chemical composition and the homogeneity of the crystals were tested by electron probe micro-analysis. Crystals characterization was performed using polarized light microscopy and dielectric and piezoelectric measurements. Phase transitions were determined by differential scanning calorimetry, optical and dielectric measurements.
WOS:000088909500054
2000
39
5A
2732
2735
Gentil, S Swiss Fed Inst Technol, Dept Mat Sci, Lab Ceram, CH-1015 Lausanne, Switzerland Swiss Fed Inst Technol, Dept Mat Sci, Lab Ceram, CH-1015 Lausanne, Switzerland Univ Geneva, CH-1211 Geneva 4, Switzerland
347CJ
Cited References Count:12
REVIEWED
EPFL