High-Resolution Transmission Electron Microscopy with Bright Microsecond Electron Pulses
Transmission electron microscopy at atomic-resolution is a crucial tool in a variety of fields, ranging from materials science to biology. [1,2] Fast electron cameras have recently enabled high-speed observations atomic resolution. [3] Moreover, they have made it possible to correct for sample drift by recording high-resolution micrographs as movies. Even higher time resolution, can be achieved by imaging with short electron pulses. [4–6] Yet, the potential of electron pulses for atomic-resolution imaging has largely remained unexplored. This is in part due to the difficulty of generating pulses that are both intense enough to the capture the image information in a short amount of time, but also coherent enough, to allow for atomic-resolution imaging. Here, we demonstrate the generation of intense, high-brightness electron pulses of microsecond duration from a Schottky field emitter whose emission current we temporarily drive to near its limit. [7] We show that such pulses enable drift-corrected imaging at atomic resolution in the presence of large amounts of drift. [8] Furthermore, they allow us to capture atomic-resolution snapshots of fast, irreverible processes, which we use to elucidate the mechanism of the high-temperature amorphization of perovskite nanocrystals. [8] As illustrated in Fig. 1, we generate electron pulses by illuminating the Schottky emitter of our microscope with a microsecond laser pulse (532 nm), which briefly heats the emitter tip to an estimated temperature of 2500 K (Ref. 7), well beyond the typical safe operating temperature. This temporarily boosts the emission current to near its limit (almost four times) and increases the brightness of the electron beam by a factor of 1.7, without damaging to the emitter. The laser-boosted electron beam is then chopped with an electrostatic deflector to obtain pulses of microsecond duration, and as short as 100 ns. We show that such intense, high-brightness electron pulses enable drift-corrected imaging at atomic resolution in the presence of otherwise prohibitively large amounts of drift, as they are for example frequently encountered in in situelectron microscopy experiments. [9] In order to induce a reproducible drift, we irradiate the sample with a laser pulse in situ, as shown in Fig. 1b. Under such conditions, which create a drift of 9 nm/s, drift-corrected images of gold nanoparticles recorded with a continuous electron beam (25 Hz camera frame rate) appear blurry (Fig. 2a). However, if we instead deliver the same electron dose per camera frame in an intense 480 µs pulse (Fig. 2xx), lattice fringes become clearly visible. We also demonstrate the potential of our electron pulses to capture atomic-resolution snapshots of irreversible transformations of nanoparticles on the microsecond timescale. As an example, we study the mechanism of the high-tempearture amorphization of perovskite nanocrystals, a phenomenon that is associated with the degradation of their optoelectronic properties in high-power devices. [10] Under in situlaser irradiation, the perovskite nanoparticle in Fig. 2c turns amorphous (Fig. 2e). A snapshot acquired during the laser pulse (Fig. 2d) reveals details of the mechanism, showing that crystallinity is lost at the boundaries first, before the amorphization process propagates towards the bulk of the crystal. [8] P.O. and G.B. contributed equally.
2021
27
S1
2714
2717
REVIEWED
Funder | Grant Number |
FNS | 206021_183295 |
FNS | PP00P2_163681 |
H2020 | 759145 |